PBAT-Based Starch Resin Compostable Plastic Bag Raw Material DEG-102

DEG-102 is a kind of PBAT blends starch modified plastic developed in accordance with Din EN 13432, ASTM D 6400, and GB / T 19277.1. The film bags made of DEG-102 is smooth, transparent, and have a good load-bearing capacity. It can be processed on various types of film blowing machines, printing machines, bag-making machines, and sealing machines.

Additional information

Type

DEG-102

Density

1.28-1.32g/cm3

Melt index(190℃/2.16kg)

5-10g/10min

Tensile strength

≥12MPa

Elongation at break

800-1000%

Maximum load bearing capacity of bag

(460mm*(310+155)mm*0.025mm),>24h
≥5Kg

Description

Recommended blowing process parameters:

  1. drying temperature/time: 80℃/1-2h
  2. processing temperature: 135-160℃
  3. blowing ratio: ≥3:1
  4. the screw of length-diameter ratio: ≥20:1

Main application:

  • packing film
  • garbage bags
  • dog poop bags
  • shopping bags, etc.

Package/Storage:

25kg/package, transport as general chemicals. Keep it dry, in a cool place, and avoid direct sunlight.